| 초록 |
BCP powder was synthesized using microwave hydrothermal process with mixed calcium hydroxide and phosphoric acid. After using replica method, porous BCP scaffold was fabricated. PU (Poly Urethane) was used as the fugitive skeleton to fabricate the porous scaffold. BCP powder was mixed in PVB (Polyvinyl butyral) and ethanol solution and then applied to the PU foam by dip coating. After several times of coating and the subsequent oven drying the coated PU foam was burnt out at 750 °C at air to remove the PU. The resulting networked porous composites were sintered at 1250°C, 1300 °C and 1350 °C in microwave furnace for 30 minutes. Material properties of the porous bodies like compressive strength and porosity were investigated. Detailed microstructure of the BCP porous body was characterized by SEM and XRD and TEM techniques. In our experiments, the relationship between mechanical property and viscosity of powder, sintering temperature was investigated. |