| 제목 | 알루미늄 알콕사이드를 이용한 유/무기 수분 차단 막 |
| 초록 | We demonstrate an organic/inorganic hybrid thin film encapsulation for OLED using sol-gel method. Sol-gel method may be a good choice for obtaining low cost, high productivity and large area devices. We consider the inorganic moiety provides moisture barrier property, while the organic moiety improves flexibility of the hybrid layer. Gibbsite (γ-Al(OH)3), Tetraethyl orthosilicate (TEOS) and Poly(methyl methacrylate) (PMMA) were used as the organic and the inorganic moiety. Nanosized hexagonal gibbsite seed are grown from a mixture of dissolved alumina alkoxides at 85℃. TEOS solution as the precursor of SiOX in ethanol with HCl and Gibbsite solution in water were separately prepared. The solutions were then mixed and dip coated on the Pen film. We focus our attention on the effect of increasing number of interfaces on the final barrier properties. The encapsulation barrier properties of these layers are assessed using the electrical calcium test. Moisture barrier property was determined by water vapor transmission rate (WVTR) measured by Ca test at 85°C and 85% RH. Water vapor transmission rate (WVTR) of ~2 × 10-2 g/m2·day is reported, which has also high potential for flexible barrier applications. |
| 저자 | 이준영1, 이해림2, 육현진2, 이혜선2, 최세인2, 정소연1, 김명은1, 김성희1 |
| 소속 | 1성균관대, 2용화여자고등학교 |
| 키워드 | 베리어박막; 깁사이트; 유무기 |
| 원문파일 | 초록 보기 |