Development of anion exchange membranes (AEMs) with good performance, such as high conductivity, good alkaline stability and mechanical strength, has been a hot topic for the fuel cell application. Here, a novel kind of hyperbranched cross-linker decorated with quaternary ammonium groups was introduced to polybenzimidazole (PBI) membranes and QOPBI-x membranes (where x is the weight ratio of the hyperbranched cross-linker). Compared with the linear OPBI membrane (0.091 S cm(-1)), QOPBI-x membranes displayed an improved ionic conductivity (up to 0.122 S cm(-1)) at 60 degrees C after they were doped in 6 M KOH for 7 days. The KOH-doped QOPBI-x membranes also exhibited a high tensile strength (54.5-61.7 MPa) and superior alkaline stability. There is almost no decline in the ionic conductivity after being immersed in a 6 M KOH solution for 30 days. In addition, the alkaline direct methanol fuel cell (ADMFC) performance based on the KOH-doped OPBI and QOPBI-x membranes is described. The QOPBI-15 membrane displayed good performance (75.6 mW cm(-2)), which is 33.3% higher than the OPBI membrane (56.7 mW cm(-2)).