Materials Research Bulletin, Vol.46, No.12, 2450-2455, 2011
Preparation and electrochemical properties of Li-rich spinel-type lithium manganate coated LiMn2O4
Li-rich spinet-type lithium manganate (SC) coated LiMn2O4 composites were prepared and characterized by XRD, SEM, FT-IR, ICP, etc. Their charge/discharge behaviors were studied between 3.0 and 4.3 V at 40 mA g(-1) under room temperature, and the results showed that SC coated on surface of LiMn2O4 could improve cycling stability of composite electrodes. The composite (Si) containing 4.8 wt% of SC exhibited noticeably improved cycling stability, whereas the initial specific capacity was very close to that of LiMn2O4. (C) 2011 Elsevier Ltd. All rights reserved.