Anodic oxides were grown on sputter-deposited Ta in different aqueous solutions. A photoelectrochemical investigation was performed in order to estimate the band gap of the films as a function of the anodizing bath composition and formation voltage, i.e. thickness. Photoelectrochemical results provided evidence of sub-band gap photocurrent for films formed in a bath containing ammonium ions at pH 9. Elemental depth profiles obtained by glow discharge optical emission spectroscopy revealed the presence of nitrogen species in the outer part of the anodic films, which is bonded to Ta according to XPS analysis. A mechanism of nitrogen incorporation is proposed in order to account for the pH dependence of film composition. (C) 2011 Elsevier Ltd. All rights reserved.