수소주입에 따른 590 MPa급 DP강 표면층의 미소경도와 조직특성

강계명; 박재우; Kae Myung Kang; Jae-Woo Park

Korean Journal of Materials Research, Vol.20, No.11, 581-585, November, 2010

DOI10.3740/MRSK.2010.20.11.581 Export Citation

수소주입에 따른 590 MPa급 DP강 표면층의 미소경도와 조직특성

Micro-Hardnesses and Microstructural Characteristics of Surface Layer of 590MPa DP Steels According to Hydrogen Charging

강계명 ^†, 박재우

서울과학기술대학교 신소재공학과

Kae Myung Kang^†, and Jae-Woo Park

Department of Materials Science and Engineering, Seoul National University of Science and Technology, Seoul 139-743, Korea

E-mail:

High strength sheet steels for automobile are seriously compromised by hydrogen embrittlement. This issue has been continuously studied, but the field of interest, which lies between microstructural characteristics and hydrogen behavior with hydrogen charging, has not yet been thoroughly investigated. This study was done to investigate the behavior of hydrogen according to the hydrogen volume fraction on 590MPa grade DP steels, which are developed under hydrogen charging conditions as high strength sheet steels for automobiles. The penetration depths and the mechanical properties, according to charging conditions, were investigated through the distribution of micro-hardness and the microstructural observation of the subsurface zone. It was found that the amount of hydrogen trapping in 590MPa DP steels was related to the austenite volume fraction. It was confirmed that the distribution of micro-hardnesses according to the depth of the subsurface zone under the free surface showed the relationship of the depth of the hydrogen saturation between the charging conditions.

Keywords:hydrogen embrittlement DP steels;hydrogen charging;micro-hardness

[References]

Maroef I, Olson DL, Eberhart M, Edwards GR, Int. Mater. Rev., 47, 191 (2002)
Watanabe J, Takai K, Nagumo M, Tetsu-to-Hagane., 82, 947 (1996)
Hagiwara N, Oguchi N, Corrosion, 55, 503 (1999)
Hirth JP, Metall. Trans. A, 11A, 861 (1980)
Troiano AR, ASM Trans., 52, 54 (1960)
Speich GR, in Proceedings of Conference on Fundamentals of Dual-Phase Steels (Warrendale, PA, 1981), ed. Kot RA, Bramfitt BL, p. 3. (1981)
Matsumoto H, Nakassato F, Kiratomi N, Kushida T, Tsumura T, CAMP-ISIJ, 7, 1602 (1994)
Dantovich DP, Floreen S, Metall. Trans. A, 4A, 2627 (1973)
Murakami K, Yabe N, Suzuki H, Takai K, Hagihara Y, Wada Y, in Proceedings of PVP2006-ICPVT-11, 2006 ASME Pressure Vessels and Piping Division Conference, CD-MF-4-1 (Vancoucer, BC, Canada, July, 2006) p.1. (2006)
Au M, Mater. Sci. Eng., 454-455, 564 (2007)
Valentini R, Solina A, Mater. Sci. Technol., 10(10), 908 (1994)
Kim YH, Morris JW, Metall. Trans. A, 14A, 1883 (1983)

[Referenced By]

[Related Articles]

[1] Maroef I, Olson DL, Eberhart M, Edwards GR, Int. Mater. Rev., 47, 191 (2002)

[2] Watanabe J, Takai K, Nagumo M, Tetsu-to-Hagane., 82, 947 (1996)

[3] Hagiwara N, Oguchi N, Corrosion, 55, 503 (1999)

[4] Hirth JP, Metall. Trans. A, 11A, 861 (1980)

[5] Troiano AR, ASM Trans., 52, 54 (1960)

[6] Speich GR, in Proceedings of Conference on Fundamentals of Dual-Phase Steels (Warrendale, PA, 1981), ed. Kot RA, Bramfitt BL, p. 3. (1981)

[7] Matsumoto H, Nakassato F, Kiratomi N, Kushida T, Tsumura T, CAMP-ISIJ, 7, 1602 (1994)

[8] Dantovich DP, Floreen S, Metall. Trans. A, 4A, 2627 (1973)

[9] Murakami K, Yabe N, Suzuki H, Takai K, Hagihara Y, Wada Y, in Proceedings of PVP2006-ICPVT-11, 2006 ASME Pressure Vessels and Piping Division Conference, CD-MF-4-1 (Vancoucer, BC, Canada, July, 2006) p.1. (2006)

[10] Au M, Mater. Sci. Eng., 454-455, 564 (2007)

[11] Valentini R, Solina A, Mater. Sci. Technol., 10(10), 908 (1994)

[12] Kim YH, Morris JW, Metall. Trans. A, 14A, 1883 (1983)