The optimum condition for fabricating cordierite disc type filter element was deduced. Cordierite monolith was used as starting material for filter element because it has many advantages such as high thermal shock resistance and good catalytic activity compared with TiO 2 and SiC. The contents of organic additives and foaming agent were optimized to control the porosity and mechanical strength of cordierite filter. Among the required properties to be adopted as filter elements, the pressure drop and NOx removal efficiency were investigated depending on processing variables. It was found that pressure drop depends on particle size distribution of cordierite monolith and organic additives added as forming agent. The pressure drop at 5cm/sec of face velocity was in the range of 15~655mm H 2 O at room temperature. The NOx removal efficiency of catalytic filter with V 2 O 5 as catalyst was over 85% at 450 ? C .