The objective of this paper is to investigate the influence of type and dosage of recycled sand (RS) and gravel on the fresh and mechanical properties of concrete. Experimental program was conducted on concretes made with different ratio of substitutions (15, 30, 70, and 100%) of natural sand and gravel with RS and gravel. At the fresh state, slump, air content, and density were measured at the exit of the mixer, and then at 30, 60, and 90min after mixing. Tests were also performed for compressive strength at the age of 1, 7, and 28days, whereas elastic modulus measurements were done at 28days. The results indicated that maintaining the workability of recycled aggregate concrete depends on sand or gravel substitution and their rates. Up to 30min, slump values were decreased, but after that, no substantial change in slump values was observed. Air content increased and density decreased, with increasing recycled aggregate content (sand or gravel). Mechanical properties, such as compressive strength and modulus of elasticity, were lower than those of reference concrete.