White organic light emitting devices (OLEDs) with an RGB stacked multilayer structure are demonstrated. In RGB staked OLEDs, blue emitting 1,4-bis[2, 2-diphenylvinyl]biphenyl (DPVBi), green emitting quinacridone (QD), and red emitting [2,6-bis[2-[5-(dibutylamino)phenyl]vinyl]-4H-pyran-4-ylidene]propanedinitrile (DADB) were used. Through the optimization of the device structure, the pure white light emission with CIE coordinates of (0.33,0.33) at 20 mA/cm(2) was obtained, at which the color temperature and color rendering index were 5560 K and 79, respectively. Its maximum luminance was 14,000 cd/m(2) at 12.6 V, and the luminance efficiency was 1.34 lm/W at 100 cd/m(2).