In this work, tomato thin-film is used as an active natural organic layer for UV photodetector. The effects of drying temperature (60-140 degrees C) on structural, chemical, electrical and UV sensing properties of tomato thin-film have been investigated. The photodetector consists of a glass substrate/tomato thin-film active layer/interdigitated aluminium electrode structure. As the drying temperature increases, surface and density of tomato thin-film is smoother and denser with thinner physical thickness. Chemical functional groups as a function of drying temperature is evaluated and correlated with the electrical property of thin film. A comparison between dark and UV (B and C) illumination with respect to the electrical property has been revealed and the observation has been linked to the active chemical compounds that controlling antioxidant activity in the tomato. By drying the tomato thin-film at 120 degrees C, a self-powered (V = 0 V) photodetector that is able to selectively detecting UV-C can be obtained with external quantum efficiency (eta) of 2.53 x 10(-7)%. While drying it at 140 degrees C, the detector is better in detecting UV-B when operating at either 5 or -5 V with eta of 7.7384 x 10(-6)% and 8.87 x 10(-6)%, respectively. The typical response time for raising and falling for all samples are less than 0.3 s. (C) 2018 Elsevier B.V. All rights reserved.