Methyltrimethoxysilane (MTMS) and trimethylethoxysilane (TMES) as starting materials were dissolved in various types of solvents, and hydrolysis with water and polycondensation reaction were carried out using various types of catalysts to prepare non-fluorinated water-repellent coating solutions. The coating solutions were spin-coated on cold-rolled steel sheets, and thermally cured to prepare water-repellent coating films. The effect of types of catalysts and solvents on the water repellency of the resulting coating films was investigated during this process. When hydrochloric acid and nitric acid, which are strong acids, were used as catalysts, the solutions showed a white opaque state due to the aggregation of siloxane polymers. On the other hand, when acetic acid, phosphoric acid, and oxalic acid, which are weak acids, were used, they were in a stable and transparent state without precipitation. As a result, the contact angles of the coated films, prepared from hydrochloric acid and nitric acid, were 58° and 92°, respectively, showing low water repellency. On the other hand, when acetic acid, phosphoric acid, and oxalic acid were used, the contact angles of the coated films were 101°, 103° and 116°, respectively, showing high water repellency. In addition, when isopropanol and ethanol were used as solvents, phase separation occurred in the solutions due to the aggregation of siloxane polymers. On the other hand, when methanol, ethyl acetate, and methyl ethyl ketone were used as solvents, the solutions were transparent and showed a stable state without sedimentation.