Polymer(Korea), Vol.30, No.2, 140-145, March, 2006
Export Citation
이미드 곁가지로 가교되는 폴리설폰의 합성 및 필름 특성
Synthesis and Film Properties of Cross-linked Polysulfone with Imide Side Chain
이은상1, 2, 홍성권2, 김용석1, 이재흥1, 김인선3, 원종찬1, †
  • 1한국화학연구원 고분자나노소재연구팀
  • 2충남대학교 고분자공학과
  • 3(주)아이컴포넌트
Eun Sang Lee1, 2, Sung Kwon Hong3, 4, Yong Seok Kim1, Jae Heung Lee1, Insun Kim5, 4, and Jong Chan Won1, †
  • 1Polymeric Nanomaterials Lab, Korea Research Institute of Chemical Technology, Daejeon 305-600, Korea
  • 2Department of Polymer Science and Engineering, Chungnam Nam National University, Daejeon 305-764, Korea
  • 3Department of Polymer Science and Engineering, Chungnam Nam University, Daejeon 305-764, Korea
  • 4, Korea
  • 5i-Components Co., Ltd., Sungnam, Gyeonggi 463-825, Korea
E-mail:
초록
디스플레이용 기판으로 사용하고 있는 유리기판은 무겁고 깨지기 쉬우므로 이를 폴리설폰, 폴리에테르설폰, 폴리카보네이트, 폴리에틸렌테레프탈레이트 환상형 올레핀 고분자 등의 플라스틱으로 대체하는 연구가 많이 이루어지고 있다. 플라스틱 기판은 가볍고, 내충격성이 뛰어나며, 유연하고 연속가공이 가능한 장점을 가지고 있다. 그러나 여러 유기용매에 녹는 특성을 가지고 있다. 디스플레이 제조 공정에서는 여러 유기용매에 노출되므로 이에 대한 내화학성이 필요하다. 그러므로 본 연구에서는 폴리설폰에 곁가지로 이미드 가교기를 도입하여 내화학성을 향상시키는 연구를 하였다. 곁사슬기에 의해 가교된 폴리설폰 필름은 용해도 조사 결과 내화학성이 향상되었음을 확인할 수 있었다. 내화학성 측정 결과 MeOH, THF, DMSO, NMP 등의 유기용매에 불용성을 보였다. 또한 15% 이상 낮은 열팽창계수를 보여 열에 대한 치수안정성이 개선되었으며 유리 전이 온도도 이미드기의 도입에 따라 180 ℃에서 252 ℃로 증가하였다. 이와 같이 제조한 이미드 곁가지로 가교된 폴리설폰은 광학적 특성이 우수하면서도 내화학성이 뛰어나 유연성 플라스틱 기판으로 사용이 가능하다.
The most commonly available substrate material is glass in the display fabrication process. However, glass is not desirable due to its heaviness and fragility. Recently, plastics such as polysulfone (PSF), polyethersulfone (PES), polycarbonate (PC), polyethylene terephthalate (PET) and cyclic olefin polymers (COP) have been investigated to replace glass as a substrate material for display fabrication. Plastic substrates are advantageous in that they are light-weight, high impact resistance, flexibility, and ability for roll to roll manufacturing process. But many plastics have poor chemical resistance in organic solvent. The chemical resistance is also required because they are exposed to solvents for various chemical treatments during the manufacturing process. So, we have an interest in the chemical modification of PSF to improve chemical resistance. We introduced cross-linkable imide moieties using chloromethylation method for the modification of PSF which could be overcome above shortcomings for display substrate based on plastic film. We prepared the cross-linked polysulfone films which were represented chemical resistance in MeOH, THF, DMSO and NMP. The thermal properties were measured by TGA, DSC and TMA. As the results, we have confirmed to enhance of the thermal property. They had low coefficient of thermal expansion (CTE) which decreased to 15% and had increased Tg from 180 ℃ to 252 ℃. Cross-linked polysulfone films with imide side-chain had good optical properties and chemical resistance so that they could be used as flexible display substrate.
Keywords:polysulfone;imide;chloromethylation;cross-linking;plastic display substrate
  1. Warshawsky A, Kahana N, Deshe A, Gottlieb H, Aradyellin RE, J. Polym. Sci. A: Polym. Chem., 28, 2885 (1990) 
  2. Avram E, Brebu MA, Warshawsky A, Vasile C, Polym. Degrad. Stabil., 69, 175 (2000) 
  3. Moshay A, Rabeson LM, J. Polym. Sci. A: Polym. Chem., 20, 1885 (1976)
  4. Hasegawa M, Horie K, Prog. Polym. Sci, 26, 259 (2001) 
  5. Zhang Y, Lu S, Li Y, Dang Z, Xin JH, Fu S, Li G, Guo R, Li L, Adv. Mater., 17, 1056 (2005) 
  6. Yang J, Lee MH, Macromol. Res., 12(3), 263 (2004)
  7. Takeichi T, Zuo M, Hasegawa M, J. Polym. Sci. B: Polym. Phys., 39(23), 3011 (2001) 
  8. Murdey R, Stuckless JT, J. Am. Chem. Soc., 125(13), 3995 (2003) 
  9. Kreuz JA, Edman JR, Adv. Mater., 10, 1229 (1998) 
  10. Yang CP, Hsiao SH, Chen KH, Polymer, 43(19), 5095 (2002) 
  11. Yang CP, Hsiao SH, Wu KL, Polymer, 44(23), 7067 (2003) 
  12. Xu HJ, Yin J, He Y, Fang JH, Zhu ZK, Wang ZG, J. Appl. Polym. Sci., 70(8), 1605 (1998) 
  13. Clair AKS, Clair TLS, U.S. Patent, 4,603,061 (1986)
  14. Clair AKS, Clair TLS, U.S. Patent, 4,595,548 (1986)
  15. Lee ES, Hong SK, Kim YS, Lee JH, Won JC, J. Appl. Polym. Sci., submitted (2005)