Korean Journal of Chemical Engineering, Vol.23, No.6, 940-947, November, 2006
DOI10.1007/s11814-006-0012-4  Export Citation
Poly(vinylidenefluoride)-hexafluoropropylene gel electrolytes based on N-(2-hydroxyethyl)-N-methyl morpholinium ionic liquids
Sun-Hwa Yeon, Ki-Sub Kim, Sukjeong Choi, Jong-Ho Cha, Huen Lee†, Jaeseung Oh1, and Byoung-Bae Lee1
  • Department of Chemical and Biomolecular Engineering, Korea Advanced Institute of Science and Technology, 373-1 Guseong-dong, Yuseong-gu, Daejeon 305-701, Korea
  • 1LG Chemical, Ltd., PO Box 61, Daejeon 305-380, Korea
E-mail:
Poly(vinylidenefluoride)-hexafluoropropylene (PVdF(HFP))-ionic liquid gel electrolytes were prepared by using ionic liquids based on N-(2-hydroxyethyl)-N-methyl morpholinium tetrafluoroborate and N-(2-hydroxyethyl)- N-methyl morpholinium hexafluorophosphate. TGA and FT-IR analyses confirmed that the solvent, N,N-dimethylacetamide (DMAC), used for mixing the PVdF(HFP) polymer with the ionic liquid, was almost totally removed during the gelling and drying processes. SEM photographs were taken of the surface structure of the PVdF(HFP)-ionic liquid in order to evaluate the morphology of the film’s surface according to the mixing ratio, as well as the nature of the ionic liquid. The thermal behaviors of PVdF(HFP)-ionic liquid gels were observed to be similar to those of neat ionic liquids through a DSC analysis, and the compatibility between the polymer and the ionic liquid was investigated by an XRD analysis. The ionic conductivities of all the gels were 10-4-10-8S·cm-1 in a temperature range of 20 ℃ to 70 ℃.
Keywords:Ionic Liquid;Morpholinium Cation;Gel Polymer;PVdF(HFP);Ionic Conductivity
  1. Capiglia C, Saito Y, Kataoka H, Kodama T, Quartarone E, Mustarelli P, Solid State Ion., 131(3-4), 291 (2000)
  2. Cha JH, Kim KS, Choi S, Yeon SH, Lee H, Kim HS, Kim H, Korean J. Chem. Eng., 22(6), 945 (2005)
  3. Ege S, Organic chemistry structure and reactivity, third edition, D. C. Heath and Company
  4. Fuller J, Breda AC, Carlin RT, J. Electoanal. Hem., 459, 29 (1998)
  5. Kim KS, Choi S, Demberelnyamba D, Lee H, Oh J, Lee BB, Min SJ, Chem. Commun., 828 (2004)
  6. Ohno H, Yoshizawa M, Ogihara W, Electrochim. Acta, 48(14-16), 2079 (2003)
  7. Southall JP, Hubbard HV, Johnston SF, Rogers V, Davies GR, McIntyre JE, Ward IM, Solid State Ion., 85(1-4), 51 (1996)
  8. Tiyapiboonchaiya C, Macfarlane DR, Sun J, Forsyth M, Macromol. Chem. Phys., 203, 1906 (2002)
  9. Yeon SH, Kim KS, Choi S, Cha JH, Lee H, J. Phys. Chem. B, 109(38), 17928 (2005)
  10. Yeon SH, Kim KS, Choi S, Lee H, Kim HS, Kim H, Electrochim. Acta, 50(27), 5399 (2005)
  11. Yoshizawa M, Hirao M, Ito AK, Ohno H, J. Mater. Chem., 11, 1057 (2001)