N-p-n Si/SiGe/Si heterostructure has been grown by a disilane (Si2H6) gas and Ge solid sources molecular beam epitaxy system using phosphine (PH3) and diborane (B2H6) as n- and p-type in situ doping sources, respectively. X-ray diffraction (XRD) and secondary ion mass spectroscopy (SIMS) measurements show that the grown heterostructure has a good quality, the boron doping is confined to the SiGe base layer, and the Ge has a trapezoidal profile. Postgrowth P implantation was performed to prepare a good ohmic contact to the emitter. Heterojunction bipolar transistor (HBT) has been fabricated using the grown heterostructure and a common-emitter current gain of 75 and a cut-off frequency of 20 GHz at 300 K have been obtained.