Epitaxial growth of AlN has been performed by molecular beam epitaxy (MBE) with ammonia. The structural properties of materials were studied by cross-sectional transmission electron microscopy (TEM), X-ray diffraction (XRD), and atomic force microscopy (AFM). XRD and TEM diffraction pattern confirm the AlN is single crystalline 2H-polytype with the epitaxial relationship of (0001)AlNparallel to(111)Si, [11 (2) over bar0](AlN)parallel to[110](Si), [10 (1) over bar0](AlN)parallel to[11 (2) over bar](Si). Micro-Raman scattering measurement shows that the E-2 (high) and A(1) (LO) phonon mode shift 9 cm(-1) toward the low frequency, which shows the existence of large tensile strain in the AlN films. Furthermore, the appearance of forbidden A, (TO) mode and its anomalous shift toward high frequency was found and explained. (C) 2002 Elsevier Science B.V. All rights reserved.