Korean Journal of Materials Research, Vol.22, No.5, 227-236, May, 2012
다관능기를 도입한 아이오노머 필름의 기체투과 특성
Permeation Property of Ionomer Film with New Multifunctional Ionic Site
E-mail:
Ionomer is a thermoplastic that is composed of covalent bonds and ionic bonds. It is possible to use this material in processes such as injection molding or extrusion molding due to the material갽s high oil resistance, weatherproof characteristics, and shock resistance. In this study, a new ionomer having a multifunctional group was prepared by a stepwise neutralization system with the addition of acidic and salt additives. In step I, to increase the contents of the multifunctional group and the acid degree in ethylene acrylic acid (EAA), MGA was added to the ionomer resin (EAA). A new ionomer was prepared via the traditional preparation method of the ionic cross-linking process. In step II, metal salt was added to the mixture of EAA and MGA. The extrusion process was performed using a twin extruder (L/D = 40, size : .30). Ionomer film was prepared for evaluation of gas permeability by using the compression molding process. The degree of neutralized and ionic cross-linked new ionomer was confirmed by FT-IR and XRD analysis. In order to estimate the neutralization of the new ionomer film, various properties such as gas permeation and mechanical properties were measured. The physical strength and anti-scratch property of the new ionomer were improved with increase of the neutralization degree. The gas barrier property of the new ionomer was improved through the introduction of an ionic site. Also, the ionic degree of cross-linking and gas barrier property of the ionomer membrane prepared by stepwise neutralization were increased.
- Tant MR, Mauritz KA, Wilkes GL, Ionomers:Synthesis, Structure, Properties and Applications, p. 3- 31, Blackie Academic and Professional, New York (1997). (1997)
- Holden G, Kricheldorf HR, Quirk RP, Thermoplastic Elastomers, 2nd ed., p. 101, Hanser Gardner Publications, USA (1996). (1996)
- Schlick S, Ionomers: Characterization, Theory, and Applications, p., CRC Press Boca Raton, USA (1996)
- Kim SH, Kim JS, Macromolecules, 36(7), 2382 (2003)
- Kirkmeyer BP, Taubert A, Kim JS, Winey KI, Macromolecules, 35(7), 2648 (2002)
- Coates J, Interpretation of Infrared Specta, A Practical Approach, ed. R. A. Meyers, p. 10837, John Wiley & Sons, USA (2000). (2000)
- DeFlores LP, Ganim Z, Nicodemus RA, Tokmakoff A, J. Am. Chem. Soc., 131(9), 3385 (2009)
- Farrell KV, Grady BP, Macromolecules, 34(20), 7108 (2001)
- Tachino H, Hare H, Hirasawa E, Kutsumizu S, Yano S, Macromolecules, 27(2), 372 (1994)
- Yarusso DJ, Cooper SL, Macromolecules, 16(12), 1871 (1983)
- Ishioka T, Kobayashi M, Macromolecules, 23(12), 3183 (1990)
- Eisenberg A, Navratil M, Macromolecules, 6(4), 604 (1973)
- Kim JS, Jackman RJ, Eisenberg A, Macromolecules, 27(10), 2789 (1994)
- Eisenberg A, Marcromolecules, 3(2), 147 (1970)
- Huber G, Vilgis TA, Macromolecules, 35(24), 9204 (2002)
- Song JM, Luqman M, Kim JS, Shin K, J. Polym. Sci. B: Polym. Phys., 45(9), 1045 (2007)
- Hayes RA, High Modulus Ionomer for Packaging, US Patent 2009/0123613 A1, December 23 (2008). (2008)
- The Membrane Society of Korea, Membrane Separation (Basic), p. 292-302, Freedom Academy, Seoul, Korea (1996) (in Korean). (1996)
- Li NN, Fane AG, Ho WSW, Matsuura T, Advanced Membrane Technology and Applications, p. 39- 54, John Wiley & Sons, New Jersey (2008). (2008)
- Huang SL, Ruaan RC, Lai JY, J. Membr. Sci., 123(1), 71 (1997)
- Hsieh KH, Tsai CC, Tseng SM, J. Membr. Sci., 49(3), 341 (1990)
- Galland G, Lam TM, J. Appl. Polymer Sci., 50(6), 1041 (1993)
- Vaughn WL, Metal ionomer membranes for gas separation, US Patent 4,789,386, September 18 (1986). (1986)
- Kutsumizu S, Watanabe Y, Yano S, Tachino H, Hara H, Kutsuwa Y, J. Mater. Sci., 32(1), 99 (1997)
- Hammon HG, Ernst K, Newton JC, J. Appl. Polymer Sci., 21(7), 1989 (1977)
- Maki N, Tajitsu Y, Sasaki H, Packag. Tech. Sci., 20(5), 309 (2007)