Three types of climb-dissociated partial dislocations were observed by high-resolution transmission electron microscopy in monazite (LaPO4) that was indented at room temperature. Two types were found on twin boundaries, and a third in the lattice. Formation mechanisms are discussed. Glide of climb-dissociated partial dislocations that is allowed by stacking fault migration is considered.