Hexamethyldisiloxane (HMDSO) films have been deposited on bell metal using radiofrequency plasma assisted chemical vapor deposition (RF-PACVD) technique. The protective performances of the HMDSO films and their water repellency have been investigated as a function of DC self-bias voltage on the substrates during deposition. Plasma potential measurements during film deposition process are carried out by self-compensated emissive probe. Optical emission spectroscopy (OES) analyses of the plasma during deposition reveal no significant change in the plasma composition within the DC self-bias voltage range of -40 V to -160 V that is used. Raman and X-ray photoelectron spectroscopy (XPS) studies are carried out for film chemistry analysis and indicate that the impinging ion energy on the substrates influences the physio-chemical properties of the HMDSO films. At critical ion energy of 113 qV (corresponding to DC self-bias voltage of -100 V), the deposited HMDSO film exhibits least defective Si-O-Si chemical structure and highest inorganic character and this contributes to its best corrosion resistance behavior. The hardness and elastic modulus of the films are found to be bias dependent and are 1.27 GPa and 5.36 GPa for films deposited at -100 V. The critical load for delamination is also bias dependent and is 11 mN for this film. The water repellency of the HMDSO films is observed to be dependent on the variation in surface roughness. The results of the investigations suggest that HMDSO films deposited by RF-PACVD can be used as protective coatings on bell metal surfaces. (C) 2011 Elsevier B. V. All rights reserved.